Sound velocity measurements carried out between 10 and 300 K in a Pd85Pt15 single crystal at 0 and 0.29 H contents for five different propagation modes, have shown that C', C44 and CT are strongly decreased by H loading (CT=1/3(C11-C12+C44). Smaller relative changes are observed for longitudinal modes. The bulk modulus as well as the anisotropy factor turn out to be increased by H impurities. The Debye temperature at absolute zero is found to be 271±5 K for n=0 and 264 ±5 K for n=0.29.

Elastic constants of a Pd85Pt15 single crystal containing hydrogen

MARZOLA, Pasquina;
1989

Abstract

Sound velocity measurements carried out between 10 and 300 K in a Pd85Pt15 single crystal at 0 and 0.29 H contents for five different propagation modes, have shown that C', C44 and CT are strongly decreased by H loading (CT=1/3(C11-C12+C44). Smaller relative changes are observed for longitudinal modes. The bulk modulus as well as the anisotropy factor turn out to be increased by H impurities. The Debye temperature at absolute zero is found to be 271±5 K for n=0 and 264 ±5 K for n=0.29.
Hydrogen; Elastic constants; Pd/Pt
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11562/476564
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 4
social impact