LaPO4 single crystals lightly doped with Er3+, and codoped with Er3+ and Yb3+ have been grown by spontaneous nucleation in a lead phosphate flux. Absorption and luminescence spectra have been measured in the visible and near-IR regions and the excited state dynamics has been studied upon pulsed laser excitation. The obtained results have allowed the evaluation of the effective emission cross-sections around 1.5 mu m, that have been found to be similar to important oxide laser crystals doped with Er3+. Efficient visible upconversion has been observed upon excitation at 980 nm in the codoped crystals. This behaviour is attributed to Yb3+-Er3+ energy transfer processes.
Luminescence spectroscopy of Er3+-doped and Er3+, Yb3+-codoped LaPO4 single crystals
SPEGHINI, Adolfo;BETTINELLI, Marco Giovanni
2009-01-01
Abstract
LaPO4 single crystals lightly doped with Er3+, and codoped with Er3+ and Yb3+ have been grown by spontaneous nucleation in a lead phosphate flux. Absorption and luminescence spectra have been measured in the visible and near-IR regions and the excited state dynamics has been studied upon pulsed laser excitation. The obtained results have allowed the evaluation of the effective emission cross-sections around 1.5 mu m, that have been found to be similar to important oxide laser crystals doped with Er3+. Efficient visible upconversion has been observed upon excitation at 980 nm in the codoped crystals. This behaviour is attributed to Yb3+-Er3+ energy transfer processes.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.