A series of europium doped (LuxGd1-x)(2)O-3 (x = 1, 0.75, 0.5, 0.25 and 0) nanocrystalline powders were prepared using a polymer complex solution method based on a polyethylene glycol (PEG) as fuel. The samples were systematically characterized by powder X-ray diffraction, scanning and transmission electron microscopies and luminescence spectroscopy. The powders consisted of well-crystalline, cubic phase nanoparticles of 20-50 nm in size, which unit cell parameter increased with Gd content complying with Vegard's law. Upon blue light excitation all samples exhibited strong red luminescence typical of trivalent europium ion. The maximum splitting of the F-7(1) manifold changed linearly with the composition change and decreased with lowering of the crystal field strength. Relatively long lifetime values were obtained for D-5(0) (similar to 1.4 ms) and D-5(1) (similar to 120 mu s) levels. For all samples we estimated theoretical densities, refractive index coefficients, optical filling factors and Z(eff), in order to estimate the Judd-Ofelt intensity parameters and branching ratios. The calculated lifetime of D-5(0) level was in line with experimentally obtained luminescence lifetime values. Relative integrated emissions were measured on all samples and Gd2O3 sample proved to have a maximum amount of the characteristic Eu3+ luminescence

Structural and spectroscopic studies of Eu3+ doped Lu2O3-Gd2O3 solid solutions

SPEGHINI, Adolfo;BETTINELLI, Marco Giovanni;
2014-01-01

Abstract

A series of europium doped (LuxGd1-x)(2)O-3 (x = 1, 0.75, 0.5, 0.25 and 0) nanocrystalline powders were prepared using a polymer complex solution method based on a polyethylene glycol (PEG) as fuel. The samples were systematically characterized by powder X-ray diffraction, scanning and transmission electron microscopies and luminescence spectroscopy. The powders consisted of well-crystalline, cubic phase nanoparticles of 20-50 nm in size, which unit cell parameter increased with Gd content complying with Vegard's law. Upon blue light excitation all samples exhibited strong red luminescence typical of trivalent europium ion. The maximum splitting of the F-7(1) manifold changed linearly with the composition change and decreased with lowering of the crystal field strength. Relatively long lifetime values were obtained for D-5(0) (similar to 1.4 ms) and D-5(1) (similar to 120 mu s) levels. For all samples we estimated theoretical densities, refractive index coefficients, optical filling factors and Z(eff), in order to estimate the Judd-Ofelt intensity parameters and branching ratios. The calculated lifetime of D-5(0) level was in line with experimentally obtained luminescence lifetime values. Relative integrated emissions were measured on all samples and Gd2O3 sample proved to have a maximum amount of the characteristic Eu3+ luminescence
2014
Nanophosphors; Sesquioxides; Rare earths
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11562/726766
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 27
  • ???jsp.display-item.citation.isi??? 22
social impact