We report on the fabrication and characterization of planar waveguides in an Er-doped tungsten-tellurite glass by implantation of 3.5 MeV N + ions. Implantations were carried out in a wide fluence range of 1 · 10 16 8 · 10 16 ions/cm 2. Waveguides were characterized by m-line spectroscopy and spectroscopic ellipsometry. Irradiation-induced refractive index modulation saturated around a fluence of 8 · 10 16 ions/cm 2. Waveguides operating at 1550 nm were obtained in that material using 3.5 MeV N + ion implantation. © 2012 IEEE.

MeV energy N +-Implanted planar optical waveguides in Er-doped tungsten-tellurite glass operating at 1.55 μm

BETTINELLI, Marco Giovanni;SPEGHINI, Adolfo;
2012-01-01

Abstract

We report on the fabrication and characterization of planar waveguides in an Er-doped tungsten-tellurite glass by implantation of 3.5 MeV N + ions. Implantations were carried out in a wide fluence range of 1 · 10 16 8 · 10 16 ions/cm 2. Waveguides were characterized by m-line spectroscopy and spectroscopic ellipsometry. Irradiation-induced refractive index modulation saturated around a fluence of 8 · 10 16 ions/cm 2. Waveguides operating at 1550 nm were obtained in that material using 3.5 MeV N + ion implantation. © 2012 IEEE.
2012
Luminescence; lanthanides; waveguides
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11562/429174
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 22
  • ???jsp.display-item.citation.isi??? 21
social impact