Nanocrystalline Lu3Ga5O12, with average particle sizes of 40 nm, doped with a wide variety of luminescent trivalent lanthanide ions have been prepared using a sol–gel technique. The structural and morphological properties of the powders have been investigated by x-ray powder diffraction, high resolution transmission electron microscopy and Raman spectroscopy. Structural data have been refined and are presented for Pr3+, Eu3+, Gd3+, Ho3+, Er3+ and Tm3+ dopants, while room temperature excited luminescence spectra and emission decay curves of Eu3+-, Tm3+- and Ho3+-doped Lu3Ga5O12 nanocrystals have been measured and are discussed. The Eu3+ emission spectrum shows typical bands due to 5D0 →7FJ (J = 0, 1, 2, 3, 4) transitions and the broadening of these emission bands with the non-exponential behaviour of the decay curves indicates the presence of structural disorder around the lanthanide ions. Lanthanide-doped nanocrystalline Lu3Ga5O12 materials show better luminescence intensities compared to Y2O3, Gd3Ga5O12 and Y3Al5O12 nanocrystalline hosts. Moreover, the upconversion emission intensity in the blue-green region for the Tm3+- and Ho3+-doped samples shows a significant increase upon 647.5 nm excitation with respect to other common oxide hosts doped with the same lanthanide ions.

Nanocrystalline lanthanide doped Lu3Ga5O12 garnets: interesting materials for light emitting devices

GIAROLA, Marco;MARIOTTO, Gino;PICCINELLI, FABIO;BETTINELLI, Marco Giovanni;SPEGHINI, Adolfo
2010-01-01

Abstract

Nanocrystalline Lu3Ga5O12, with average particle sizes of 40 nm, doped with a wide variety of luminescent trivalent lanthanide ions have been prepared using a sol–gel technique. The structural and morphological properties of the powders have been investigated by x-ray powder diffraction, high resolution transmission electron microscopy and Raman spectroscopy. Structural data have been refined and are presented for Pr3+, Eu3+, Gd3+, Ho3+, Er3+ and Tm3+ dopants, while room temperature excited luminescence spectra and emission decay curves of Eu3+-, Tm3+- and Ho3+-doped Lu3Ga5O12 nanocrystals have been measured and are discussed. The Eu3+ emission spectrum shows typical bands due to 5D0 →7FJ (J = 0, 1, 2, 3, 4) transitions and the broadening of these emission bands with the non-exponential behaviour of the decay curves indicates the presence of structural disorder around the lanthanide ions. Lanthanide-doped nanocrystalline Lu3Ga5O12 materials show better luminescence intensities compared to Y2O3, Gd3Ga5O12 and Y3Al5O12 nanocrystalline hosts. Moreover, the upconversion emission intensity in the blue-green region for the Tm3+- and Ho3+-doped samples shows a significant increase upon 647.5 nm excitation with respect to other common oxide hosts doped with the same lanthanide ions.
2010
Nanocrystalline garnets; lanthanide ion doped; light emission devices
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11562/341931
Citazioni
  • ???jsp.display-item.citation.pmc??? 0
  • Scopus 69
  • ???jsp.display-item.citation.isi??? 64
social impact