Polycrystalline thin-film CdTe/CdS solar cells have been developed in a configuration in which a transparent conducting layer of indium tin oxide (ITO) has been used for the first time as a back electrical contact on p-CdTe. Solar cells of 7.9% efficiency were developed on SnOx:F-coated glass substrates with a low-temperature (<450°C) high-vacuum evaporation method. After the CdCl2 annealing treatment of the CdTe/CdS stack, a bromine methanol solution was used for etching the CdTe surface prior to the ITO deposition. The unique features of this solar cell with both front and back contacts being transparent and conducting are that the cell can be illuminated from either or both sides simultaneously like a 'bi-facial' cell, and it can be used in tandem solar cells. The solar cells with transparent conducting oxide back contact show long-term stable performance under accelerated test conditions.

CdTe solar cells in a novel configuration

ROMEO, Alessandro;
2004-01-01

Abstract

Polycrystalline thin-film CdTe/CdS solar cells have been developed in a configuration in which a transparent conducting layer of indium tin oxide (ITO) has been used for the first time as a back electrical contact on p-CdTe. Solar cells of 7.9% efficiency were developed on SnOx:F-coated glass substrates with a low-temperature (<450°C) high-vacuum evaporation method. After the CdCl2 annealing treatment of the CdTe/CdS stack, a bromine methanol solution was used for etching the CdTe surface prior to the ITO deposition. The unique features of this solar cell with both front and back contacts being transparent and conducting are that the cell can be illuminated from either or both sides simultaneously like a 'bi-facial' cell, and it can be used in tandem solar cells. The solar cells with transparent conducting oxide back contact show long-term stable performance under accelerated test conditions.
2004
thin film; flexible cells; CdTe; Solar cells
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11562/306684
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 92
  • ???jsp.display-item.citation.isi??? 85
social impact